Component | Description | Part No. |
---|---|---|
Special Clear Hardener | 207-QT (27 oz.) | 207-SB |
WEST SYSTEM brand resins and hardeners, form a two-part epoxy system developed by Gougeon Brothers specifically for wood and composite construction. WEST SYSTEM epoxy is recommended by Rutan Aircraft Factory for certain homebuilt aircraft applications, particularly where a moisture resistant epoxy is desired. 105 Resin is the base material on which all of the WEST SYSTEM epoxy systems are built. The resin is a clear, light amber, low-viscosity liquid. It is designed specifically to wet out wood fiber. With roller applications, it possesses excellent thin film characteristics in flowing out and is self-leveling without fish-eyeing. Its relatively high flash point makes it safer to work with than polyesters. It can be cured in a wide temperature range, then sanded and shaped. It cures quite clear so that the natural finish shines through.
205 Fast Hardener, when mixed with the 105 Resin in a ratio of 5 parts Resin to 1 part Hardener, yields a high-strength, rigid solid with excellent cohesive properties and provides an excellent moisture vapor barrier. The 105 Resin/205 Fast Hardener has a pot life of 10-15 minutes at 70°F. It is also recommended in coating applications where natural finishing is desired. Partial cure time at 70°F is 5-7 hours. 206 Slow Hardener is a low-viscosity mixture of polyamines. The 105 Resin/206 Slow Hardener has a pot life of 30-40 minutes at 70°F. It is normally used when extended time is needed for large coating and bonding applications. It is especially well suited to working in warmer climates. Partial cure time is 9 hours at 70°F. Order by size and hardener. Pump sold separately. |
Super easy to measure out using the mini pump kit (a must!) and mixes well, dries rock hard, and clear, flows good, used for glassing model rocket plywood fins, a great product!
Such an amazing product! Used this epoxy system to fibreglass the hull of a scale RC boat that Im scratch building. There is virtually no odour to this product compared to the polyester resins I have used in the past. The mini-pumps are the best dispensing system and so easy to use. I am sold and will continue using this product any time I need a great epoxy.
Quick delivery and as ordered.
Excellent product
I like the ease of the West measurement with the pumps.
great resin for my fiberglass projects. It mixes easily and sets up very nicely. Sands fairly easy and seems to have good strength.
Best epoxy Ive ever used!
The Right Stuff for the composite work thats an inevitable part of RV kit construction. Used it for 22 years and no complaints.
Works as advertised , quick delivery from Spruce as usual
Please note, Aircraft Spruce Australia's personnel are not certified aircraft mechanics and can only provide general support and ideas, which should not be relied upon or implemented in lieu of consulting an A&P or other qualified technician. Aircraft Spruce Australia assumes no responsibility or liability for any issue or problem which may arise from any repair, modification or other work done from this knowledge base. Any product eligibility information provided here is based on general application guides and we recommend always referring to your specific aircraft parts manual, the parts manufacturer or consulting with a qualified mechanic.
This system has a max Tg of 116 degrees Farenheit. For all other technical information, please see the Tech Data Sheet located in the "Documents" tab of this web page.
The West Systems epoxy does not have a haz mat charge if shipped domestic USA ground service.
In general, epoxies are not recommended for use with fiberglass mat material. Uni or Bi directional woven cloth only.
The 205 hardener will have a pot life at 72F/22C: 9 to 12 minutes. The 206 hardener will have a pot life at 72F/22C 20 to 25 minutes.
Shelf life foe the West Systems 105 system is as follows:
Store at room temperature. Keep containers closed to prevent contamination. With proper storage, resin and hardeners should remain usable for many years. After a long storage, verify the metering accuracy of the pumps. Mix a small test batch to assure proper curing.
Over time, 105 Resin will thicken slightly and will therefore require extra care when mixing. Repeated freeze/thaw cycles during storage may cause crystallization of 105 Resin. Warm the resin to 125°F and stir to dissolve crystals.
Hardeners may darken with age, but physical properties are not affected by color. If clear finishing, be aware of possible color shift if very old and new hardeners are used on the same project.
If you mix the hardener and resin you have a working time of 10-15 minutes for the fast and 30-40 minutes for the slow. The resin and hardener have a shelf life of 3 years.